Water over quenched
ROC Mn contains 11 - 14 % Manganese, over quenched, fully austenitic and then is non-magnetic, work hardening steel with an exceptionally high level of wear resistance when subjected to impact or high pressure in service.
Internationals standards: EN: X120Mn12 or WN°: 1.3401 or HADFIELD
|Thicknesses (mm)||Formats (mm)|
|2 - 30||1000 × 2000
1500 × 3000
2000 × 6000
Typical values (weight %).
|≤ 1.35||≤ 14||≤ 0.20||≤ 0.035||≤ 0.035|
Mechanical properties in delivery conditions
|Hardness (HB)||UTS (MPa)||YS (MPa)||E (%)|
Only with plasma or laser.
Cold bending and rolling are easy to perform (at workshop temperature >10 °C). It is not recommended to form in any area, hardened due to shearing operation (grinding requested).
Please contact us for any machining aspect.
Use stainless welding products (class AWS A5.4 E 307 or 5.4 E 3.8MO).
|Thickness range (mm)||Size range (mm)|
|3 - 30||W: 1000 × 3000 / L: up to 6000|