An innovative grade with very high performance taking its inspiration from the chemistry of Creusabro 8000 and being re-inforced with titanium carbides. The ultimate solution for severe sliding abrasion combined with great impact. For applications where conventional water quenched steels (500HB, 550HB), hardfacing plates or hard-casting parts are traditionally implemented.

450-520 HB
Thickness : 8-50 mm | Format: 2000x6000 / 2500x8000 mm

Application: Bucket liners for excavator, shovel, loader, dozer, cutting edges, truck body liners, wear parts for primary and secondary crushers, vibratory feeder liners...

Creusabro 8000 is a wear resistant steel that combines extreme resistance to abrasion together with a high level of toughness. The ability of this grade to work harden offers an increase of up to 45% service life compared to conventional 500 HB materials.

500-540 HB
Thickness : 5-60 mm | Format: 2000x6000 / 2500x8000 mm

Application: Cement plant, quarrying, mining & earth moving equipment, steel production, recycling plant...

Creusabro 4800 is a wear resistant steel that combines extreme resistance to abrasion together with a high level of toughness. The ability of this grade to work harden offers an increase of up to 45% service life compared to conventional 400 HB materials. It also works at higher temperatures than standard abrasion steels, continuously at >400 ºC.

500-540 HB
Thickness : 3-100 mm | Format: 1500x3000 / 1500x6000 / 2000x6000 / 2500x6000 mm

Application: Block moulds, cement plants, quarrying, mining & earth moving equipment, steel production, recycling plant...

A steel with good abrasion resistance, improved processing, heat resistance <400°C, mechanical safeguards - use at room temperature.

270-350 HB
Thickness : 4-80 mm | Format: 2000x6000 / 2500x6000 mm

Application: a multi-purpose steel for all wear situations.

A steel with good abrasion resistance, improved processing, heat resistance <400°C, mechanical safeguards - use at room temperature.

270-350 HB
Thickness : 10-50 mm | Format: 2000x6000 mm

Application: a multi-purpose steel for all wear situations.

A water quenched abrasion resistant plate with a hardness of 400 HB and can be readily welded and fabricated.

370-430 HB
Thickness : 10-60 mm | Format: 1500x3000 / 2000x6000 mm

Application :Earthmoving and loading equipment, buckets and edges, dredgers, conveyors, knives and shears, skip liners, recycling equipment, agricultural machinery...

Dillidur Impact is a wear resistant steel with exceptionally high resistance to cracking. It has a nominal hardness of approximately 340 HBW in its delivered condition, and its outstanding mechanical properties are obtained by water quenching and subsequent tempering. Dillidur Impact is successfully applied where high resistance to abrasion is required together with very high toughness to resist impact wear.

310-370 HB
Thickness : 10-60 mm | Format: 1500x3000 / 2000x6000 mm

Application: Earthmoving and loading machines, cutting edges, buckets, shovels, grabs, scoops, breakers and knives...

High chromium carbide weld overlay plate, which offers high resistance to sliding abrasion under moderate impact conditions and temperatures between 450 and 650 ° C.

58 to 62 HRC + / -2 HRC
Thickness: 5+3 / 6+4 / 8+5 / 10+9 mm | Format: 1250x2500 / 1500x3000 / 2000x3000 mm

A carbon manganese (11-14%), hyper-quenched austenitic, non-magnetic, work hardening steel plate. Outstanding resistance to abrasion with frontal impacts or high compression.

550 - 600HB (after hardening)
Thickness: 3-30 mm | Format: 1000x2000 / 1500x3000 / 2000x6000 mm

Application: impact and transfer plates (mines and quarries), liners (shot blasting cabinets), lock mechanism protection for security doors...

Wear resistant water quenched grade, which can be readily welded and fabricated.

450-550 HB
Thickness: 6-30 mm | 2000x6000 mm

Wear resistant water quenched grade, which can be readily welded and fabricated.

370-430 HB
Thickness: 5-25 mm / Format: 1500x6000 mm
Thickness: 5-60 mm / Format: 2000x6000 mm

Application: general use for any parts subjected to abrasion.

Abrasion-resistant steel from strip mill production. Excellent surface condition for a satisfactory appearance after painting.

340-440 HB
Thickness: 3-8 mm / Format:1250x6000 / 1500x6000 mm

Application: general use for any parts subjected to abrasion

Wear resistant standard plate, suitable for welding.

280-345 HB
Thickness: 3-50 mm | Format: 1000x2000 / 2000x6000 mm

Application: production of components for mining and quarrying.

An economical wear resistant solution for simple cases of abrasion, good machinability.

200-260 HB
Thickness: 4-40 mm | Format: 1500x3000 / 2000x6000 mm

Application: general purpose grade for limited abrasion.

Duplex stainless steel type, excellent corrosion resistance (equivalent to AISI 316) and good abrasion resistance (equivalent steel hardness 300 HB).

260 HB
Thickness: 4-20 mm | Format: 2000x6000 mm

Application: where abrasion and severe corrosion are combined...

Normalized steel particularly suited for resistance to combined abrasion & corrosion in wet environments.

Abrasion resistance at temperatures up to 600 ° C.

300-320 HB
Thickness: 4-20 mm | Format: 2000x6000 mm

Application: steel, cement, sugar, mining, fertilizer production...

Ferritic stainless steel type. A technical and economic solution in the case of combined, limited abrasion & corrosion. Good resistance to temperature <500 ° C and a good slip coefficient with good resistance to clogging.

220 HB
Thickness: 3-20 mm | Format: 1500x3000 / 2000x6000 mm

Application: petrochemical, sugar refining, paper, mining and quarrying, agriculture...

Steel resistant to atmospheric corrosion.

220 HB
Thickness: 3-20 mm | Format: 1500x3000 / 1500x6000 mm / 2000x6000 mm

Steel moulds for pavers, suitable for nitriding.

HB 200 (state of delivery)
62 HRC + / - 2 HRC after heat treatment

Application: concrete block mould parts to withstand severe abrasion with fatigue (repeated sequences of vibrations).